Oxide wire bond insulation in semiconductor assemblies

ABSTRACT

A semiconductor integrated circuit package is provided with insulated bonding wires. The semiconductor die is mounted to a base of either a leadframe or a grid-array package. A plurality of bonding wires are bonded between bonding pads on the semiconductor die and bonding fingers at inner ends of package conductors. The bonding wires have an oxygen-plasma oxide formed thereupon to thereby provide electrically-insulated bonding wires to prevent short-circuits between adjacent bonding wires. After wire bonding of the bonding wires, the bonding wires are subjected to an oxygen plasma to form an insulating oxide on the bonding wires to prevent short-circuits with adjacent wires. The wires are aluminum or copper with an oxygen-plasma oxide formed thereupon. An oxygen-plasma oxide is simultaneously formed on a leadframe and is removed from the outer ends of the leads by blasting with a medium.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to packaging of semiconductor devices and, more particularly, to techniques for insulating bonding wires during assembly of an integrated-circuit package.

2. Prior Art

The trend in integrated circuit packaging is to have the spacing between bonding pads on an integrated circuit die become smaller so that the pitch of the bonding pads gets tighter. For this reason and for other reasons, such as this use of multiple bonding tiers, the length of the bonding wires in IC packages are getting longer and longer bonding wires have a tendency to electrically short-circuit together.

Various attempts have been made to electrically insulate bonding wires to avoid having adjacent wires touching each other and electrically short-circuit. One technique provides insulation on the wires prior to wire bonding. Insulating the bonding wires prior to bonding created problems such as modification of wire-bonding machines, increased costs, decreased yields, and charring of the insulation material which contaminates the integrated-circuit die.

Another technique provides for coating the bonding wires with a silicone spray after wire bonding. Using this so-called "wet" technique, the sprayed silicone material can get on the leadframe or substrate on which the die is mounted. During encapsulation of the die and bonding wires, this silicone material causes a loss of adhesion of the encapsulating material to the leadframe or substrate. This silicone spray also prevents good adhesion of plating materials on the leadframe.

Consequently, a need exists for a dry technique for electrically insulating bonding wires to prevent electrical short circuits therebetween.

SUMMARY OF THE INVENTION

It is therefore an object of the invention to provide a technique for providing electrical insulation to the bonding wires of an integrated-circuit package during assembly of the package to prevent electrical short circuits between adjacent bonding wires in the integrated-circuit package.

In accordance with these and other objects of the invention, a semiconductor integrated-circuit die is singulated and die-attached to the leadframe or a substrate. Wire bonds are formed between the die and the package leads using aluminum or copper bonding wires. Next, the wire-bonded ICs are subjected to an oxygen plasma process where energetic oxygen ions bombard the aluminum or copper bonding wires and the leads to produce an insulating layer of aluminum oxide or copper oxide on the bonding wires. The assembly is then encapsulated as either a molded plastic package, a grid-array package including a glob-top package, or a pin-grid array package. For a molded plastic package with a leadframe, the oxide is then removed from the leads of a molded plastic package by a media-blasting process and the leads are plated with Pb/Sn coating.

A method is provided according to the invention for packaging a semiconductor integrated circuit with insulated bonding wires. The method includes: attaching a semiconductor die to a mounting base and wire-bonding a plurality of aluminum or copper bonding wires between respective bonding pads on the semiconductor die and respective bonding fingers at the inner ends of leads of a leadframe. After wire bonding, the bonding wires are subjected to an oxygen plasma to form an aluminum oxide on the plurality of bonding wires to thereby provide electrically-insulated bonding wires to prevent short-circuits between adjacent bonding wires of the package. For a package with a leadframe, the leads are also subjected to the oxygen plasma to form an oxide on the leads. The semiconductor die, the bonding wires, and the bonding fingers are encapsulated to expose the oxidized outer ends of the leads. The oxide on the exposed outer ends of the leads of the leadframe are removed by blasting with a media. For a grid-array package, such as a ball-grid array package or a pin-grid array package, a die is mounted to a polymer substrate and the bonding wires are attached to conductors formed on the polymer substrate. The bonding wires are then subjected to an oxygen plasma to provide an insulating oxide thereupon.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are incorporated in and form a part of this specification, illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention:

FIG. 1 is a sectional view showing a bonding wire connected between a bonding pad on an integrated-circuit die and a bonding finger of a leadframe of a molded plastic package assembly.

FIG. 2 is a sectional view showing apparatus using an oxygen plasma for growing an Al₂ O₃ aluminum oxide layer on bonding wires of the molded plastic package assembly.

FIG. 3 is a sectional view showing formation of the Al₂ O₃ aluminum oxide layer on the aluminum bonding wire and bonding pad and also showing formation of an oxide layer on the bonding finger of the leadframe of the molded plastic package assembly.

FIG. 4 is a sectional view showing encapsulation of the semiconductor die, the bonding wires, and the inner end of the bonding finger to expose the oxidized outer end of the lead of the molded plastic package assembly.

FIG. 5 is a sectional view showing apparatus for removal of the oxide on the exposed outer end of the lead of the leadframe of the molded plastic package assembly by blasting with a media.

FIG. 6 is a sectional view showing the step of plating the exposed outer end of the lead of the leadframe of the molded plastic package assembly with a Pb/Sn coating.

FIG. 7 is a sectional view showing the step of forming the outer end of the lead of the molded plastic package assembly.

FIG. 8 is a sectional view showing a bonding wire connected between a bonding pad on an integrated-circuit die and a copper trace of a grid-array package.

FIG. 9 is a sectional view showing apparatus using an oxygen plasma for growing an insulating layer on bonding wires of the grid-array package.

FIG. 10 is a sectional view showing formation of an insulating layer on the bonding wire of the grid-array package.

FIG. 11 is a sectional view showing encapsulation of the semiconductor die, the bonding wires, and the inner end of the copper trace to expose the outer end of the lead grid-array package.

FIG. 12 is a sectional view showing attachment of solder balls to the grid-array package.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Reference will now be made in detail to the preferred embodiments of the invention, examples of which are illustrated in the accompanying drawings. While the invention will be described in conjunction with the preferred embodiments, it will be understood that they are not intended to limit the invention to these embodiments. On the contrary, the invention is intended to cover alternatives, modifications and equivalents, which may be included within the spirit and scope of the invention as defined by the appended claims.

FIG. 1 shows a structure which includes singulated semiconductor integrated-circuit die 10 mounted to a suitable mounting base 12 such as a die-attach pad or a separate substrate with a layer 14 of an appropriate bonding material, such as a silver-filled epoxy material. The substrate 12 is a die-attach pad of a leadframe or, optionally, a separate thermally conductive substrate. A bonding wire 16 has one end ultrasonically bonded to a bonding pad 18 on the top surface of the integrated-circuit die 10. The top surface of the die 10 is covered with a protective oxide layer 20 having openings provided over the bonding pad 18. The other end of the bonding wire is ultrasonically bonded to a bonding finger 22 at the inner end of a lead 24 of the leadframe. The bonding wire 16 is typically made of a conductive material such as aluminum or copper, which can be oxidized to form an insulating layer on the surface of the bonding wire. The bonding pad 18 on the die is typically made of aluminum and the leadframe is typically made of copper or silver-plated copper.

FIG. 2 illustrates an oxygen-plasma process for forming an insulating layer on the structure of FIG. 1. The dotted arrows represent energetic O- ions in an oxygen plasma surrounding the structure.

FIG. 3 illustrates the result of subjecting the structure of FIG. 1 to the oxygen plasma environment of FIG. 2. The energetic O- ions in the plasma react at the surface of the aluminum or copper bonding wire 16 to form an insulating coating 25 of aluminum oxide or copper oxide on the bonding wire 16. The insulating coating 25 on each of a plurality of bonding wires in a package provide electrical insulation between adjacent bonding wires in order to prevent electrical short-circuits, or shorts, therebetween.

The energetic O- ions in the plasma also react at the surface of the copper or silver-coated leadframe to form an insulating coating 26 of copper oxide or silver oxide on the leads and die-attach pad of the leadframe. An oxide coating is also formed on the aluminum bonding pad 18.

FIG. 4 illustrates a molded plastic package body 28 formed of a plastic molding compound material. The molded package body 28 encapsulates the semiconductor die 10, the insulated bonding wire 16, and the inner end of the bonding finger 22. The oxide layer 26 at the outer ends of the lead 24 is exposed after this encapsulation.

FIG. 5 illustrates apparatus for removal of the oxide layer 26 on the exposed outer end of the lead 20 of the leadframe shown in FIG. 4. A series of nozzles, typically shown as 30, are used to direct a high power jet using a media such as a mixture of water and glass beads, typically shown as 32, for blasting away the oxide layer 26 at the outer ends of the lead 24.

FIG. 6 illustrates the exposed outer end of the lead 24 having a Pb/Sn coating 34 formed thereupon. FIG. 7 illustrates the lead 24 of the molded plastic package being bent to a suitable profile, such as, for example, a gull wing configuration.

FIG. 8 illustrates a package structure for a grid-array package which includes a singulated semiconductor integrated-circuit die 40 mounted and attached to a die-attach pad portion 42 of a conductive copper layer with a layer 44 of an appropriate bonding material, such as a silver-filled epoxy material. The copper layer extends over an insulated substrate 46 formed, for example, of a polymer material, such as an epoxy or polyimide material. The copper layer includes a plurality of peripheral conductive traces, typically shown as 48. A top solder mask 50 is formed over the copper trace 48 with openings over the inner ends thereof. A bottom solder mask 52 extends over the lower surface of the epoxy substrate 46 with openings formed therein through which extend gold-plated conductive pads 54, 55 for connection to solder balls in a ball-grid array package. Grid-array packages also include pin-grid array packages where the pads 54, 55 are replaced with projecting pins.

A typically-illustrated bonding wire 56 has one end ultrasonically bonded to a bonding pad 58 formed on the top surface of the integrated-circuit die 40. The other end of the bonding wire 56 is ultrasonically bonded to a bonding area 60 at the inner end of the conductor area 48. The bonding wire 56 is typically made of a conductive material, such as aluminum or copper, which can be oxidized to form an insulating layer on the surface of the conductor. The bonding pad 58 is typically made of aluminum which is oxidized to form an insulating layer thereupon.

FIG. 9 illustrates an oxygen-plasma process for forming an insulating layer on the bonding wire 56 of FIG. 8, where the dotted arrows represent energetic O- ions in an oxygen plasma surrounding the structure for the grid-array package.

FIG. 10 illustrates the result of subjecting the structure of FIG. 8 to the oxygen plasma environment of FIG. 9. The energetic O- ions in the plasma react at the surface of the aluminum or copper bonding wire 56 to form an insulating coating 62 of aluminum oxide or copper oxide on the bonding wire 56 to provide electrical insulation between adjacent bonding wires in order to prevent electrical short-circuits, or shorts, therebetween. The energetic O- ions in the plasma do not react at the gold surface of the gold-plated conductive pads 54, 55, leaving them ready to have solder balls attached thereto.

FIG. 11 illustrates a glob-top package body 64 formed of an epoxy material to encapsulate the semiconductor die 40, the insulated bonding wire 56, and the inner end of the bonding area 60 at the inner end of the conductor area 48. FIG. 12 illustrates attachment of solder balls 66, 67 to the conductive pads 54, 55 of the grid-array package. It is intended that the grid-array package, such as a pin-grid array package, are provided with oxidized insulated bonding wires in accordance with the present invention.

The foregoing descriptions of specific embodiments of the present invention have been presented for purposes of illustration and description. They are not intended to be exhaustive or to limit the invention to the precise forms disclosed, and obviously many modifications and variations are possible in light of the above teaching. The embodiments were chosen and described in order to best explain the principles of the invention and its practical application, to thereby enable others skilled in the art to best utilize the invention and various embodiments with various modifications as are suited to the particular use contemplated. It is intended that the scope of the invention be defined by the Claims appended hereto and their equivalents. 

What is claimed is:
 1. A method of packaging a semiconductor integrated circuit with insulated bonding wires, comprising the steps of:attaching a semiconductor die to a mounting base; wire-bonding respective first ends of a plurality of aluminum bonding wires to respective bonding pads on the semiconductor die; wire-bonding respective second ends of the plurality of aluminum bonding wires to respective bonding fingers at inner ends of leads of a leadframe; after wire bonding of the respective first and second ends of the plurality of aluminum bonding wires, subsequently subjecting the bonding wires to an oxygen plasma and forming an electrically-insulated aluminum oxide on the plurality of aluminum bonding wires to thereby provide electrically-insulated bonding wires to prevent short-circuits between adjacent bonding wires; simultaneously subjecting the leads of the leadframe to the oxygen plasma and forming an oxide on the leads of the leadframe; encapsulating the semiconductor die, the bonding wires, and the bonding fingers to expose the oxidized outer ends of the leads of the leadframe; and removing the oxide on the exposed outer ends of the leads of the leadframe.
 2. The method of claim 1 wherein the step of attaching the semiconductor die to the mounting base includes attaching the semiconductor die to a die-attach pad of the leadframe.
 3. The method of claim 1 wherein the step of attaching the semiconductor die to the mounting base includes attaching the semiconductor die to a separate substrate.
 4. The method of claim 1 wherein the step of removing the oxide on the exposed outer ends of the leads of the leadframe includes blasting away the oxide on the exposed outer ends of the leads of the leadframe with a media jet.
 5. The method of claim 1 including the step of plating the exposed outer ends of the leads of the leadframe with a Pb/Sn coating.
 6. The method of claim 1 wherein the step of encapsulating the semiconductor die and the bonding wires includes molding a plastic package body around the semiconductor die, the bonding wires, and the bonding fingers.
 7. A method of packaging a semiconductor integrated circuit with insulated bonding wires, comprising the steps of:attaching a semiconductor die to a mounting base; wire-bonding respective first ends of a plurality of metal bonding wires to respective bonding pads on the semiconductor die; wire-bonding respective second ends of the plurality of metal bonding wires to respective package conductors; and after wire bonding of the respective first and second ends of the plurality of metal bonding wires, subsequently subjecting the bonding wires to an oxygen plasma and forming an electrically-insulated oxide on the plurality of metal bonding wires to thereby provide electrically-insulated bonding wires to prevent short-circuits between adjacent metal bonding wires.
 8. The method of claim 7 wherein the step of attaching a semiconductor die to a mounting base includes attaching the semiconductor die to a die-attach pad of a leadframe.
 9. The method of claim 7 wherein the step of attaching the semiconductor die to the mounting base includes attaching the semiconductor die to a separate substrate.
 10. The method of claim 7 wherein the steps of wire-bonding the first and second ends of the plurality of bonding wires includes wire-bonding a plurality of aluminum bonding wires and wherein the step of subjecting the bonding wires to an oxygen plasma and forming an oxide includes forming an aluminum oxide on the aluminum bonding wires.
 11. The method of claim 7 wherein the steps of wire-bonding the first and second ends of the plurality of bonding wires includes wire-bonding a plurality of copper bonding wires and wherein the step of subjecting the bonding wires to an oxygen plasma and forming an oxide includes forming a copper oxide on the copper bonding wires.
 12. The method of claim 7 wherein the step of wire-bonding respective second ends of the plurality of bonding wires to respective package conductors includes wire bonding to the bonding fingers of a leadframe.
 13. The method of claim 12 including the step of simultaneously subjecting the leads of the leadframe to the oxygen plasma and forming an oxide on the leads of the leadframe.
 14. The method of claim 13 including the steps of:encapsulating the semiconductor die, the bonding wires, and the bonding fingers to expose the oxidized outer ends of the leads of the leadframe; and removing the oxide from the exposed oxidized outer ends of the leads of the leadframe.
 15. A method of packaging a semiconductor integrated circuit with insulated bonding wires in a grid-array package, comprising the steps of:mounting a semiconductor die to an insulated grid-array substrate; wire-bonding respective first ends of a plurality of aluminum bonding wires to respective bonding pads on the semiconductor die; wire-bonding respective second ends of the plurality of aluminum bonding wires to respective inner ends of conductive traces formed on the substrate; after wire bonding of the respective first and second ends of the plurality of aluminum bonding wires, subsequently subjecting the aluminum bonding wires to an oxygen plasma and forming an electrically-insulated aluminum oxide on the plurality of aluminum bonding wires to thereby provide electrically-insulated bonding wires to prevent short-circuits between adjacent bonding wires; and encapsulating the semiconductor die, the bonding wires, and the bonding fingers with a packaging material.
 16. The method of claim 15 including the step of providing gold-plated solder-ball pads on the substrate of a ball-grid array package and encapsulating with a glob-top epoxy material.
 17. The method of claim 15 wherein the step of mounting the semiconductor die to the substrate includes mounting the semiconductor die to a polymer substrate.
 18. The method of claim 16 including mounting the semiconductor die to a polymer substrate wherein the polymer material is selected from the group comprising an epoxy material and a polyimide material. 